Features:
| Model No. | Chemical Composition(%) | True Density | Apparent Density | Grain Size D50 | +325 Mesh | Original Crystal D50 | Features | Recommended Applications | ||||
| Al2O3 ≥% | SiO2 ≤% | Fe2O3 ≤% | Na2O ≤% | LOI ≤% | g/cm3 ≥ | g/cm3 ＞ | D50 (μm) | ＜% | D50(μm) | |||
| CA1A | 99.5 | 0.05 | 0.03 | 0.10 | 0.1 | 3.97 | >0.95 | ~70 | \ | 5.0-6.0 | 1. High temperature calcination 2. Low sodium 3. Large crystal 4. High conversion rate 5. Stable shrinkage. Good fluidity 6. High insulation performance 7. High mechanical strength |
1. High-performance ceramics, such as vacuum tubes 2. Especially suitable for hot -pressing casting process |
| CA1D | 99.5 | 0.05 | 0.03 | 0.08 | 0.1 | 3.95 | >0.90 | \ | 3.0-4.0 | 1. Low sodium 2. Moderate crystal size 3. Good particle size distribution 4. Small shrinkage and stability |
1. Spark plugs 2. Vacuum tubes 3. Wear-resistant ceramics, etc. 4. More suitable for static pressure, dry-pressing and other forming processes |
|
| CA1 | 99.5 | 0.05 | 0.03 | 0.10 | 0.1 | 3.95 | >0.90 | \ | 3.0-3.8 | 1. Static kiln calcination 2. Low sodium 3. Moderate crystal size 4. Good particle size distribution 5. High porcelain density |
1. Mainly used in electronic ceramics 2. Especially suitable for Hot die casting process |
|
| CA2 | 99.5 | 0.08 | 0.03 | 0.08 | 0.1 | 3.96 | >0.90 | \ | 2.8-3.8 | 1. Low sodium 2. Strict crystal size control 3. Good fluidity 4. Stable shrinkage |
1. Electronic ceramics, structural ceramics 2. Especially suitable for Hot die casting process |
|
| CA2G | 0.15 | >0.90 | 3.0-3.5 | < 3.0 | 1. CA2 full grinding 2. Particle size control stability 3. Low sodium 4. Shrinkage stability |
1. Electronic ceramics 2. Structural ceramics, more suitable for making ceramic rollers |
||||||
| CA3 | 99.5 | 0.05 | 0.03 | 0.04 | 0.1 | 3.96 | >0.85 | ~70 | \ | 2.0-2.6 | 1. Strict control of firing temperature 2. Small crystal size 3. Good particle distribution 4. Pretty-low sodium |
Suitable for electronic ceramics, such as IC substrates |
| CA3G | 0.1 | 2.4-2.9 | <1.0 | Fully grinding of CA3 | ||||||||
| CA4 | 99.5 | 0.05 | 0.03 | 0.10 | 0.1 | 3.93 | >0.90 | ~70 | \ | 1.0-1.8 | 1. Good activity 2. Low sodium 3. High density after firing 4. Stable shrinkage 5. High mechanical strength |
1. Structural ceramics 2. Electronic ceramics 3. 99 alumina ceramic granulation powder material 4. Suitable for extrusion molding process as well |
| CA4G | 0.1 | >0.60 | 1.5-2.2 | <1.0 | Fully grinding of CA4 | |||||||
| CA5 | 99.5 | 0.05 | 0.02 | 0.05 | 0.1 | 3.92 | ~70 | \ | ＜1.0 | 1. Small & unifrom crystal size 2. Good activity |
99 alumina ceramic hot die casting process, etc | |
| CA5G | 1-1.3 | <1.0 | 1. Small & unifrom crystal size 2. Good activity 3. Fully grinding 4. Narrow particle size distribution |
Ceramic filter,etc | ||||||||
Usually will be around 99.5%,also customized service will be supported.
Per different requirements from customers,there're 0.1%, 0.04%, 0.05%, 0.08%,etc.
Based on your requirements, there are various options available for you to choose from, including products suitable for processes like hot pressing casting, static pressure, dry pressing, or hot die casting, among others.
Fill in your needs in the form below We will reply you E-mail as soon as possible.
We will solve the problem for you within 24 hours